بررسی اثر ورودی حرارت فرآیند GTAW بر ریزساختار و گسترش HAZ اتصالات جوشکاری فولادی HSLA-100 با استفاده از چرخه های حرارتی
نوع مقاله : مقاله پژوهشی
نویسندگان
10.22034/ijissi.2021.243777
[1] B. K. Show, R. Veerababu, R. Baramuralikrishnan, G. Malakondaiah: Mater. Sci. Eng. A., 527(2010), 1595.
[2] Y. Liu, L. Shi, C. Liu, L. Yu, Z. Yan, H. Li: Mater. Sci. Eng. A., 675(2016), 371.
[3] S. Vervynckt, K. Verbeken, B. Lopez, J.J. Jonas: Int. Mater. Rev., 57(2012), 187.
[4] S. K. Dhua, D. Mukerjee, D. S. Sarma: Metall. Mater. Trans. A., 34(2003), 2493.
[5] S. K. Dhua, D. Mukerjee, D. S. Sarma: Metall. Mater. Trans. A., 32(2001), 2259.
[6] S. Das, A. Ghosh, S. Chatterjee, P. R. Rao: Scand. J. Metall., 31(2002), 272.
[7] M. Mujahid, A. K. Lis, C. I. Garcia, A. J. Deardo: J. Mater. Eng. Perform, 7(1998), 247.
[8] E. J. Czyryca, M. G. Vassilsros: Ship. Mater. Eng. Depart. Res. Develop. Rep., 1993.
[9] G. Thewlis: Mater. Sci. Technol, 20(2004), 143.
[10] S. Kou: Welding metallurgy, John Wiley and Sons, New Jersey, (2003), 145.
[11] S. S. Babu: Curr Opin Solid State Mater Sci, 8(2004), 267.
[12] X. J. Di, X. An, F. J. Cheng, D. P. Wang, X. J. Gou, Z. K. Xue: Sci. Technol. Weld. Join, 21(2016), 366.
[13] Y. Li, T. N. Baker: Mater. Sci. Technol., 26(2010), 1029.
[14] G. Spanos, D. W. Moon, R.W. Fonda, E. S. K. Menon, A. G. Fox: Metall Mater Trans A, 32(2001), 3043.
[15] K. Prasad, D. Dwivedi: Int. J. Adv. Manuf. Technol., 36(2008), 475.
[16] B. Beidokhti. A.H. Koukabi, A. Dolati: Mater Charact, 60(2009), 225.
[17] M. Shome: Mater. Sci. Eng. A., Vol (2007), 454.
[18] M. Shome, O. N. Mohanty: Metall Mater Trans A, 37(2006), 2159.
[19] H. Dong, X. Hao, D. Deng: Metallogr. Microstruct. Anal., 3(2014), 138.
[20] ASME Sec IX, American Society of mechanical engineers: Qualification Standard for Welding and Brazing Procedure, Article II, Welding Procedure Qualification, 2015.
[21] E. Girault, P. Jacques, Ph. Harlet, K. Mols, J.Van Humbeeck, E. Aernoudt, F. Delannay: Mater Charact, 40(1998), 111.
[22] ASTM E112, American Society for Testing and Materials: Standard test method for determining average grain size, 2004.
[23] S. S. Ghasemi banadkouki, D. P. Dunne: ISIJ Int., 46(2006), 759.
[24] O. Grong, D. K. Matlock: Int. Met. Rev., 31(1986), 27.
[25] Z. Zhang, R.A. Farrar: Mater. Sci. Technol., 12(1996), 237.
[26] J. M. Dowling, J. M. Corbett, H .W. Kerr: Metall. Mater. Trans. A., 17(1986), 1611.
[27] S. Panwar, D. B. Goel, O.P. Pandey, K. Satya Prasad: Bull. Mater. Sci., 29 (2006), 281.
[28] L. Lan, C, Qiu, D. Zhao, X. Gao, L. Du: J. Mat. Sci., 47(2012), 4732.
[29] I. A. Yakubtsov, J. D. Boyd: Mater. Sci. Technol., 17(2001), 296.
[30] H. Inoue, T. Koseki, S. Okita, M. Fuji: Weld. Int., 12(1998), 195.
[31] H.J. Jun, J.S. Kang, D.H. Seo, K.B. Kang, C. G. Park: Mater. Sci. Eng. A., 422(2006), 157.
[32] X. Li, C. Shang, X. Ma, B. Gault, S.V. Subramanian, J. Sun, R.D.K. Misra: Scr. Mater., 139(2017), 67.
[33] S. Moeinifar, A. H. Kokabi, H. R. Madaah Hosseini: Mater. Des., 31(2010), 2948.
[34] C. Sun, S. Yang, G. Liu: Acta Metall. Sin(Engl. Lett.), 27(2014), 426.
[35] S. D. Bhole, A. G. Fox: Can. Metall. Q., 35(1996), 151.
[36] A. Lambert-perlade, A.F. Gorgoues, J. Besson, T. Sturel, A. Pineau: Metall. Mater. Trans. A., 35(2004), 1039.
[37] S. Moeinifar, A. H. Kokabi, H .R. Maadaah Hosseini: J Mater Process Technol, 211(2011), 368.
[38] S. Moeinifar, A. H. Kokabi, H. R. Madaah Hosseini: Mat. Des., 31(2010), 2948.
[39] K. W. Andrews: ISIJ Int., 203(1965), 721.
)