Iron & Steel Society of Iran International Journal of Iron & Steel Society of Iran 2981-0388 10 2 2013 12 01 The Layered Reduction of Hematite (Iron Oxide) Ore by Non-Coking Coal: The Effect of Calcium Carbonate on Reduction The Layered Reduction of Hematite (Iron Oxide) Ore by Non-Coking Coal: The Effect of Calcium Carbonate on Reduction 23 29 10653 EN A. Shakiba Department of Material Science and Metallurgy, Amirkabir University of Technology, Tehran, Iran. Kh. Edalati Department of Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran J. Vahdati-Khaki Department of Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran A. Zabet Department of Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. Journal Article 2014 12 02 Due to the abundance of the non-coking coal and limitations as well as the high costs of the natural gas, the present study examined the direct reduction of hematite (iron oxide) ore in the temperature range of 800-1000 °C by the non-coking coal volatiles. Approximately, 74.9% of the total amounts of volatiles and gases exit the coal up to 800°C. The onset temperature to exit volatiles from the non-coking coal was approximately 525°C. The SEM micrographs and XRD results indicated the non-uniform layered reduction of the hematite layer. As temperature was increased, the reduction of hematite ore was increased. At a constant temperature of 1000°C, the reduction rate of the hematite layer reached a maximum after 30 min and then it was decreased. Adding various amounts of calcium carbonate to the non-coking coal in optimal reduction conditions increased the reduction rate of the hematite ore. The optimal concentration of this catalyst was 5 wt% (relative to the coal). https://journal.issiran.com/article_10653_4bf9cd0c47aeb311049c6f5bafd85269.pdf