TY - JOUR ID - 5473 TI - Effect of Aluminum on Microstructure and Thickness of Galvanized Layers on Low Carbon silicon-Free Steel JO - International Journal of Iron & Steel Society of Iran JA - IJISSI LA - en SN - 2981-0388 AU - Parvini Ahmadi, N. AU - Rafiezadeh, E. AD - Faculty of Materials Engineering, Sahand University of Technology, Tabriz, Iran. AD - Faculty of Materials Engineering, Sahand University of Technology, Tabriz, Iran Y1 - 2009 PY - 2009 VL - 6 IS - 1 SP - 25 EP - 29 KW - Hot Dip Galvanizing KW - Aluminum KW - Alloy layers DO - N2 - In hot dip galvanizing, several parameters such as chemical composition of coating bath, immersion time and surface roughness of specimens could affect microstructure and properties of coating. In this article, the effect of aluminum content, immersion time and surface roughness on structure and properties of alloy layers have been investigated. Specimens of low carbon silicon-free steel with different surface roughness were galvanized in pure zinc bath and bath containing various amounts of aluminum for different times. It was found that the morphology of deposits was changed from layered to columnar state when 0.025wt%Al was added into coating bath. By increasing Al content up to 0.05wt%Al the adherence of the layers was improved but these thicknesses were decreased due to reduction of diffusion rate.  UR - https://journal.issiran.com/article_5473.html L1 - https://journal.issiran.com/article_5473_1e1ec04690ae0cd4e3b4a8ac94a1bae5.pdf ER -