Effects of Martensite Reversion Parameters on the Formation of Nano/ultrafine Grain Structure in AISI 304L Stainless Steel

Esfandiary, Hojjat; Hosseini, S. R.; Ashrafizadeh, F.; Kermanpour, A.

Effects of Martensite Reversion Parameters on the Formation of Nano/ultrafine Grain Structure in AISI 304L Stainless Steel

Document Type : Research Paper

Authors

Hojjat Esfandiary ¹

S. R. Hosseini ²

F. Ashrafizadeh ¹

A. Kermanpour ¹

¹ Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156- 83111, Iran

² Department of Materials Engineering, Maleke-ashtar University of Technology, Isfahan 83145-115, Iran

Abstract

Formation of nano/ultrafine grain structure in AISI 304L austenitic stainless steel through the martensite reversion treatment was studied. The solution annealed specimens were cold rolled up to 95 % thickness reduction at -15°C. The cold-rolled specimens were subjected to reversion annealing treatment at the temperature range of 700-1000 °C for 10–150 min. Microstructural evolutions were analyzed using ferritscopy, X-ray diffraction, and field emission scanning electron microscopy techniques, whereas mechanical properties were determined by hardness test. The saturation strain during cold rolling was about 56 % reduction. The mean austenite grain size of 135 nm was obtained by 95 % cold reduction and annealing at 700 °C for 10 min. It was found that increasing cold reduction resulted in grain refinement at the same condition of reversion annealing and higher hardness.

Keywords

Nano/ultrafine

Stainless steel

Cold work

Reversion annealing